Solution for pipeline electrophoresis paint
Product Introduction :
HS-6060BLB Color Epoxy acrylic Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, aluminum products, and stainless steel sheet etc. It is widely used in the electrophoresis coating of spring, hardware, home appliance, stationery, auto parts, electric car, groove pipe fittings etc.
This product features shown below :
| The appearance of the coating is flat, delicate, smooth, uniform high gloss |
| Good stability of bath can adaptable for a longer updating cycle |
| The bath has strong anti-shrinkage and anti-pollution ability |
| Strong anti-corrosion properties |
| Coating fullness of good, better substrate hiding |
Main ingredients :
| Matrix resin: acrylic modified epoxy resin | Curing agent: totally enclosed multi-isocyanates |
| Neutralizing agent: organic acid | Solvent: alcohol ether |
| Additives: surface active agent, prevent shrinkage cavity agent | Pigment: Titanium pigment, Organic pigment, kaolin, antirust pigment |
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000～4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(180-185)℃×(20-30)min (Keeping temperature of parts coated)
Customers in the pipeline industry :
Product Tags:
|
|
Pipeline Black Edp Coating , Electrolysis Painting With Alcohol Ether Main Ingredients Images
|